Polyether

GL-3000

50 Max

52.0 ~ 56.0

0.1 Max

5.5 ~ 8.0

0.1 Max

480~540

KE-7083

50 Max

54.0 ~ 56.5

0.05 Max

5.5 ~ 7.0

0.1 Max

470~530

KE-7084

-

50.5 ~ 54.5

0.05 Max

5.5 ~ 7.0

0.1 Max

490~590

KE-7085

-

48.5 ~ 52.5

0.05 Max

5.5 ~ 7.0

0.1 Max

600~700

KE-851

-

36.5 ~ 39.5

0.5 Max

6.0 ~ 7.5

0.1 Max

2000~3000

KE-861

-

35.5 ~ 39.0

0.3 Max

6.0 ~ 7.5

0.1 Max

2000~4000

KONIX GL-3000 is an ethylene oxide-tipped polyether with primary hydroxyl group. It is particularly useful as an ingredient of blended polyethers for hot-molded flexible urethane foams. It is usually applied in blending with a polyether having secondary hydroxyl group such as GP-3000 polyether with the prescribed mixing ratio. It has high reactivity group and consequently, is highly productive in the molding process.

KONIX KE-7083, KE-7084, KE-7085 produce foams with excellent skin-feeling. They have a wide range of variation in using tin catalyst in the foaming formulation and give higher efficiency in curing compared with other polyols, and are particularly suitable for producing the urethane foams with a slightly soft touch.

KONIX KE-851, KE-861 are specially designed polymer polyol for the production of molded flexible urethane foam. When employed in combination with such polyether as KONIX KE-7083, GL-3000 etc, for producing highly resilient molded foams, they give foams with a wide range of hardness. KE-851, KE-861 are suitable for producing dual-hardness seat foam.